- This study focuses on investigating carbonitride coatings, specifically CNTi-(Zr, ZrNb, and ZrSi), as promising candidates for enhancing the durability and efficiency of Ti6Al4V materials used in nuclear fusion technology. X-ray diffraction analysis identified distinct phases, including TiN, ZrN, ZrC, and TiC. The corrosion studies showed complete degradation of the TiN, ZrC, and ZrN phases in the TiZrCN coating after tests, while the TiC phase exhibited relative stability. The surface morphologies and elemental mapping analysis demonstrated the loss of homogeneity in element distribution after corrosion process. The addition of Si and Nb elements into TiZrCN significantly influenced the coatings' corrosion behavior, with breakaway corrosion observed in CNTi- (Zr and ZrSi) coatings and localized corrosion in CNTi-(ZrNb) coatings. Notably, the CNTi-(ZrSi) coating formed an oxide phase in the presence of NaCl, whereas the CNTi-(ZrNb) coating exhibited continuous resistance and a lowThis study focuses on investigating carbonitride coatings, specifically CNTi-(Zr, ZrNb, and ZrSi), as promising candidates for enhancing the durability and efficiency of Ti6Al4V materials used in nuclear fusion technology. X-ray diffraction analysis identified distinct phases, including TiN, ZrN, ZrC, and TiC. The corrosion studies showed complete degradation of the TiN, ZrC, and ZrN phases in the TiZrCN coating after tests, while the TiC phase exhibited relative stability. The surface morphologies and elemental mapping analysis demonstrated the loss of homogeneity in element distribution after corrosion process. The addition of Si and Nb elements into TiZrCN significantly influenced the coatings' corrosion behavior, with breakaway corrosion observed in CNTi- (Zr and ZrSi) coatings and localized corrosion in CNTi-(ZrNb) coatings. Notably, the CNTi-(ZrSi) coating formed an oxide phase in the presence of NaCl, whereas the CNTi-(ZrNb) coating exhibited continuous resistance and a low corrosion rate. Irradiation was carried out for the generation of active isotopes, showing that no radioactive isotopes were formed in any of the investigated samples.…